ALTECH® PA66 A 3040/100 GB40
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA66 A 3040/100 GB40 is a base polymer composed of Polyamide 66 and 40% glass beads. It can be processed through injection molding at a melt temperature of 280-300°C and a mold temperature of 80-100°C. It is suitable for the automotive, electrical, and electronic markets and is used for various injection molded parts, such as easy release (demolding) and low warpage. To ensure optimal performance, it should be stored dry and protected from light, not above 30°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Features
- Good Mold Release, Low Warpage
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Bead
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Material Features
- Good Mold Release
- Low Warpage
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 5000.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 140.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 5200.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 75.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 3.4 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 25.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1440.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 120.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.7 - 0.9 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.8 - 1 | % | ISO 294-4 |