ALTECH® PA6/6T B 4030/219 MR30 IM
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA6/6T B 4030/219 MR30 IM is a Polyphthalamide-based polymer containing a mineral filler/additive system that is highly heat stabilized, elastomer modified, and features easy release (demolding), low warpage, injection molding grade, and good flow with low water absorption. It should be protected from light and stored at a temperature below 30°C. For best results, processing injection molding should be done at a melt temperature of 310-330°C and a mold temperature of 70-100°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Features
Elastomer Modified, Good Flow, Good Mold Release, Heat Stabilized, Low Warpage, Low Water Absorption
- Synonyms
- Methylsulfonic Acid
- Functions
- Resin
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Mineral
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Elastomer Modified
- Good Flow
- Good Mold Release
- Heat Stabilized
- Low Warpage
- Low Water Absorption
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 4000.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 110.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 4400.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 70.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 4.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 105.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 80.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1350.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 110.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 295.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.03 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 0.75 mm) | HB | class | UL 94 |
| UL Recognition (Dry) | yes | — | — |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 310 - 330 | °C |
| Mould Temperature | 70 - 100 | °C |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR, Dry) | 5.0 | cm³/10min | ISO 1133 |
| MVR Temperature (Dry) | 325.0 | °C | — |
| MVR Load (Dry) | 5.0 | kg | — |