To catalogue
ALTECH® PA66 A 2030/578 GF30
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA66 A 2030/578 GF30 is a heat-stabilized polyamide 66 with a 30% glass fiber filler/additive system. It should be pre-dried at 80°C in a dry air (desiccant) dryer for 2-12 hours depending on moisture content, with a maximum moisture content of 0.15%. It should be processed with an injection molding machine with a melt temperature of 280-300°C and a mold temperature of 80-120°C. Typical applications include housings and various injection-molded parts.
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALTECH
- Features
- Good Flow, Good Mold Release, Heat Stabilized
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 8400.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 245.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 9100.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 180.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.8 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 35.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 7.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1380.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 245.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 264.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 0.75 mm) | HB | class | UL 94 |
Table 6 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |