ALTECH® PC A 1000/500

CAS Number: 7757-83-7
Chemical Family: Polycarbonate (PC)

MOCOM Compounds ALTECH® PC A 1000/500 is a polycarbonate-based product with easy flow, heat stabilization, and easy release (demolding) features. It is suitable for various injection-molded parts. Before processing, it should be pre-dried under 120°C in a dry air (desiccant) dryer for 2-3 hours, or in an air circulating dryer at 100-120°C for 4-12 hours depending on the moisture content, with a maximum moisture content of <0.02%. During processing, it should be injection-molded at a melt temperature of 270-310°C and a mold temperature of 80-110°C. After processing, it should be protected from light and stored at a temperature not exceeding 30°C.

Product families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Other characteristics

Brand: ALTECH
Synonyms: Na2SO3,Sodium Sulfite
Functions: Resin
Polymer Name: Polycarbonate (PC)
Labeling Claims: Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
Flexural Modulus: 2650.0 - 2650.0 MPa
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Technology: Plastics
Material Features: Good Flow
Good Mold Release
Heat Stabilized
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In an air circulatIng dryer 100-120 °C for 4-12 h; Dependant on moisture content; 120 °C in a dry air (dessiccant) dryer for 2-3 h
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

7 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2650.0	MPa	ISO 178
Flexural Strength	105.0	MPa	ISO 178
Tensile Modulus	2500.0	MPa	ISO 527
Tensile Stress at Yield	65.0	MPa	ISO 527
Tensile Elongation at Yield	6.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	no break	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	12.0	kJ/m²	ISO 179/1eA

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1200.0	kg/m³	ISO 1183

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Vicat B50	140.0	°C	ISO 306
HDT / A (1.8 MPa)	125.0	°C	ISO 75-1/-2

Table 4 of 6