ALTECH® PC A 1000/121 UV IM

Chemical Family: Polycarbonate (PC)

MOCOM Compounds ALTECH® PC A 1000/121 UV IM should be pre-dried under conditions of 120°C in a dry air (dessiccant) dryer for 2-3 hours, or in an air circulating dryer at 100-120°C for 4-12 hours depending on moisture content, with a maximum moisture content of 0.02%. For processing through injection molding, the melt temperature should be set between 270-310°C, and the mold temperature between 80-110°C. The base polymer is polycarbonate, and the filler/additive system is UV stabilized and impact modified. Typical applications are varied, and the product should be handled with care to avoid damage.

Product families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Other characteristics

Brand: ALTECH
Features: Impact Modified, UV Resistant, UV Stabilized
Functions: Resin
Polymer Name: Polycarbonate (PC)
Labeling Claims: Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
Additives Included: Impact Modifier, UV Stabilizer
Impact Modifier
UV Stabilizer
Processing Methods: Injection Molding
Technology: Plastics
Material Features: Impact Modified
UV Resistant
UV Stabilized
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In an air circulatIng dryer 100-120 °C for 4-12 h; 120 °C in a dry air (dessiccant) dryer for 2-3 h; Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

6 rows

Characteristic	Value	Unit	Method
Tensile Modulus	2300.0	MPa	ISO 527
Tensile Stress at Yield	59.0	MPa	ISO 527
Tensile Elongation at Yield	5.5	%	ISO 527
Tensile Elongation at Break	60.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	no break	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	50.0	kJ/m²	ISO 179/1eA

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1200.0	kg/m³	ISO 1183

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Vicat B50	140.0	°C	ISO 306
HDT / A (1.8 MPa)	130.0	°C	ISO 75-1/-2

Table 4 of 6