ALTECH® PP-B A 4930/507 MR30
MOCOM Compounds ALTECH® PP-B A 4930/507 MR30 is a Polypropylene Heterophasic Copolymer containing 30% talcum and is specially designed for building and construction, machinery, and household goods applications. It is highly heat stabilized and has easy release (demolding) and slip agent properties. Pre-Drying Conditions should be carried out in a dry air (dessiccant) dryer at 80-120°C for 2-3 hours or in an air circulating dryer at 80-120°C for 2-4 hours. Processing Injection molding should be carried out at a melt temperature of 200-250°C and a mold temperature of 20-70°C. The product should be stored in a cool, dry place and should not be exposed to temperatures above 30°C.
Product families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Features
- Good Mold Release, Heat Stabilized
- Functions
- Resin
- Polymer Name
- Polypropylene Copolymer
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Mineral, Talc
- Mineral
- Talc
- Additives Included
- Heat Stabilizer, Slip Agent
- Heat Stabilizer
- Slip Agent
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Housewares
- Technology
- Plastics
- Material Features
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Construction Applications
- Containers
- Household Goods
- Kitchenware
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2900.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 38.0 | MPa | ISO 178 |
| Tensile Modulus | 3100.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 25.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 2.8 | % | ISO 527 |
| Tensile Elongation at Break | 22.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 43.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 3.5 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1120.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 84.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 76.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 166.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 250 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 13.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 1.3 - 1.7 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 1.1 | % | ISO 294-4 |