ALTECH® PA6 A 1000/106
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA6 A 1000/106 is a polyamide 6 base polymer with fast solidifying, easy release (demolding), and easy flow properties. It is suitable for use in injection molding, with a melt temperature of 250-270°C and a mold temperature of 40-80°C. Pre-drying conditions should be maintained at 80°C in a dry air (dessiccant) dryer for 2-12 hours, depending on moisture content, with a maximum moisture content of 0.15%. Typical applications include housings and handles. To ensure product quality and consistency, it is necessary to perform regular quality checks.
Product families
Applications
- Interior
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Features
- Fast Solidifying, Good Flow, Good Mold Release
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Fast Solidifying
- Good Flow
- Good Mold Release
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Interior Parts
- Handles
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 2600.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 85.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 3300.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Dry) | 85.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Dry) | 3.6 | % | ISO 527 |
| Tensile Elongation at Break (Dry) | 9.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 285.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1160.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 (Dry) | 200.0 | °C | ISO 306 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 3 mm) | V - 2 | class | UL 94 |
Table 6 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 40 - 80 | °C |