ALTECH® PP-H A 1000/120 UV
- Chemical Family
- PolyolefinsPolypropylenes (PP)
MOCOM Compounds ALTECH® PP-H A 1000/120 UV is a polypropylene homopolymer with special features including UV stabilization, easy release (demolding), processing stabilization, and heat stabilization. It is used for electrical and electronic applications such as electrical components, injection molded parts, and consumer electronics. Typical applications include functional components and housings.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Housings & Enclosures
Product Families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Additives Included
Heat Stabilizer, Processing Stabilizer, UV Stabilizer; Heat Stabilizer; Processing Stabilizer; UV Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Mold Release
- Heat Stabilized
- Processing Stability
- UV Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Electrical Components
- Electrical/Electronic Applications
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 1100.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 26.0 | MPa | ISO 178 |
| Tensile Modulus | 1200.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 28.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 12.3 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 14.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 1.5 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 910.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 80.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 62.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 166.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 240 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 28.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 1.2 - 1.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.6 - 2 | % | ISO 294-4 |