ALTECH® PA6 B 1000/270
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA6 B 1000/270 is a Polyamide 6 base polymer with good flow and easy release (demolding) properties, making it suitable for use in the building and construction market segment. It is typically used for housings, clips, and functional components in exterior parts and injection molded parts.
Product families
Applications
- EIFS & Insulation
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Flexural Modulus
- 2700.0 - 2700.0 MPa
- Processing Methods
- Injection Molding
- Certifications & Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS), EC No.1907/2006, IATF 16949, ISO 13485, ISO 14001, ISO 17025, ISO 45001, ISO 50001, ISO 9001, REACH (Europe), REACH (UK), RoHS Compliant, SVHC Compliant
- Markets
- Building & Construction
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Good Flow
- Good Mold Release
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Clips
- Construction Applications
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2700.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 90.0 | MPa | ISO 178 |
| Tensile Modulus | 3000.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 85.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 3.8 | % | ISO 527 |
| Tensile Elongation at Break | 20.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 75.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1130.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 65.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 220.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.2 - 1.6 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.4 - 1.8 | % | ISO 294-4 |