ALTECH® PC A 1000/572 UV
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds ALTECH® PC A 1000/572 UV is a polycarbonate-based polymer with a UV stabilized special feature and a release agent filler/additive system. It is typically used for applications in sport and leisure and should be stored in a dry and protected environment not exceeding 30°C. For processing injection molding, a melt temperature of 270-310°C and a mold temperature of 80-110°C is required. No additional sentence is needed.
Product families
- Polycarbonates
Other characteristics
- Brand
- ALTECH
- Functions
- Resin
- Polymer Name
- Polycarbonate (PC)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Additives Included
- Release agent, UV Stabilizer
- Release agent
- UV Stabilizer
- Processing Methods
- Injection Molding
- Certifications & Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS), EC No.1907/2006, IATF 16949, ISO 13485, ISO 14001, ISO 17025, ISO 45001, ISO 50001, ISO 9001, REACH (Europe), REACH (UK), RoHS Compliant, SVHC Compliant
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Material Features
- UV Resistant
- UV Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In an air circulatIng dryer 100-120 °C for 4-12 h; Dependant on moisture content; 120 °C in a dry air (dessiccant) dryer for 2-3 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2500.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 75.0 | MPa | ISO 178 |
| Tensile Modulus | 2400.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 62.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 6.0 | % | ISO 527 |
| Tensile Elongation at Break | 100.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 12.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 12.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1210.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 144.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 131.0 | °C | ISO 75-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 310 | °C |
| Mould Temperature | 80 - 110 | °C |
Table 7 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 13.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | 0.5 - 0.8 | % | ISO 294-4 |