ALTECH® PA6 A 2015/327
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA6 A 2015/327 is a polyamide 6 reinforced with 15% glass fibers that has been UV stabilized and impact modified for easy demolding. This product is commonly used in the automotive, building, and construction markets for applications such as cooling systems, fuel systems, gear wheels, roller bearings, and injection molded parts. It is typically used for oil pump parts, bearings, sliding elements, engine covers, and housings.
Product families
Applications
- Fuel Systems
- Powertrain & UTH
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Features
Good Mold Release, Impact Modified, UV Resistant, UV Stabilized
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber
- Additives Included
- Impact Modifier, UV Stabilizer
- Impact Modifier
- UV Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Good Mold Release
- Impact Modified
- UV Resistant
- UV Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Construction Applications
- Cooling System
- Engine Covers
- Gear Wheels
- Housings
- Oil Pump Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 4900.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 2300.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 170.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 62.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 5400.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 2600.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 110.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 4.0 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 59.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 11.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 60.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 90.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1230.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 195.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.3 - 0.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 0.9 | % | ISO 294-4 |