TEDUR® L 9560 S
- Chemical Family
- Polyphenylene Sulfide (PPS)
MOCOM Compounds TEDUR® L 9560 S is a Polyphenylene Sulfide injection molding grade with 50% mineral filler/additive system. It has improved surface appearance, high surface gloss, and is metallizable. Pre-drying conditions include drying in a dry air (dessiccant) dryer for 2-4 hours depending on moisture content at 130-140°C. Processing injection molding requires a melt temperature between 320-340°C and a mold temperature above 140°C. Typical applications include reflectors for automotive, lighting and consumer products.
Product families
Applications
- Aftermarket Parts & Components
- Exterior & Body
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- TEDUR
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Mineral
- Flexural Modulus
- 8500.0 - 8500.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Chemical Resistant
- Good Flow
- Good Surface Appearance
- Good Surface Gloss
- High Temperature Resistance
- Low Thermal Expansion
- Metallizable
- Wide Temperature Operating Range
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 130-140 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 8500.0 | MPa | ISO 178 |
| Flexural Strength | 110.0 | MPa | ISO 178 |
| Tensile Modulus | 8500.0 | MPa | ISO 527 |
| Flexural Deflection (Maximum Force) | 1.4 | % | ISO 178 |
| Tensile Strength at Break | 75.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 15.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1820.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 145.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 280.0 | °C | ISO 11357 |
Table 4 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (0.75 m) | V - 0 | class | UL 94 |
| Flammability (1.5 mm) | V - 0 | class | UL 94 |
| Flammability (3.0 mm) | V - 0 | class | UL 94 |
| Glow Wire (GWFI, 960°C, 2mm) | Passed | — | DIN EN 60695 |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | min. 140 | °C |
| Melt Temperature | 320 - 340 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.8 - 1 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 0.9 | % | ISO 294-4 |