TEDUR® L 9421-1 S
- Chemical Family
- Polyphenylene Sulfide (PPS)
MOCOM Compounds TEDUR® L 9421-1 S is a blend of Polyphenylene Sulfide and 40% glass fibers, 10% PTFE, which has improved sliding/wear, high stiffness, and high toughness properties. It is used in Automotive and Machinery markets for bearings and sliding elements, functional components. The pre-drying conditions involve drying in a dry air (dessiccant) dryer at 130-140°C for 2-4 hours, depending on moisture content. The processing injection molding involves a melt temperature of 320-340°C and a mold temperature greater than 140°C.
Product families
- High Performance Thermoplastics
Other characteristics
- Brand
- TEDUR
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 14200.0 - 14200.0 MPa
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Excellent Toughness
- Good Flow
- Good Sliding Properties
- High Stiffness
- High Temperature Resistance
- Improved Wear
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 130-140 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 14200.0 | MPa | ISO 178 |
| Flexural Strength | 250.0 | MPa | ISO 178 |
| Tensile Modulus | 15700.0 | MPa | ISO 527 |
| Flexural Deflection (Maximum Force) | 1.9 | % | ISO 178 |
| Tensile Strength at Break | 180.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.7 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1730.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 275.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 280.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | V - 0 | class | UL 94 |
| Glow Wire (GWFI, 960°C, 2mm) | Passed | — | DIN EN 60695 |
Table 5 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | min. 140 | °C |
| Melt Temperature | 320 - 340 | °C |