TEDUR® L FC 9510-7
- Chemical Family
- Polyphenylene Sulfide (PPS)
MOCOM Compounds TEDUR® L FC 9510-7 is a polyphenylene sulfide-based polymer containing 40% glass fibers, making it ideal for injection molding due to its high stiffness, easy flow and reduced flash. It is suitable for applications in the machinery, electrical and electronic, and building and construction markets, such as housings and parts in contact with drinking water.
Product families
Applications
Building & Construction — Building Materials
- Pipes & Plumbing
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- TEDUR
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 13500.0 - 13500.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Building & Construction
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Drinking Water Contact Acceptable
- Good Flow
- High Stiffness
- High Temperature Resistance
- Low Flash
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 130-140 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Construction Applications
- Electrical/Electronic Applications
- Housings
- Machine/Mechanical Parts
- Pump Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 13500.0 | MPa | ISO 178 |
| Flexural Strength | 260.0 | MPa | ISO 178 |
| Tensile Modulus | 14500.0 | MPa | ISO 527 |
| Flexural Deflection (Maximum Force) | 2.1 | % | ISO 178 |
| Tensile Strength at Break | 160.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.7 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 40.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1650.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 275.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 280.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | 1 x 10¹² | Ohm | DIN EN 62631-3-2 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | V - 0 | class | UL 94 |
| Glow Wire (GWFI, 960°C, 2mm) | Passed | — | DIN EN 60695 |
Table 6 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | min. 140 | °C |
| Melt Temperature | 320 - 340 | °C |