TEDUR® L 9214-1

Chemical Family: Polyphenylene Sulfide (PPS)

MOCOM Compounds TEDUR® L 9214-1 is a base polymer of polyphenylene sulfide with a filler/additive system of 45% glass fibers and 20% mineral. It is designed for highly stressed parts in the automotive and machinery market segments, and has special features of high stiffness. Pre-drying conditions include a dry air (dessiccant) dryer at 130-140°C for 2-4 hours depending on moisture content. Processing includes injection molding with a melt temperature of 320-340°C and a mold temperature greater than 140°C.

Product families

Applications

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: TEDUR
Polymer Name: Polyphenylene Sulfide (PPS)
Fillers Included: Glass Fiber, Glass/Mineral, Mineral
Glass Fiber
Glass/Mineral
Mineral
Flexural Modulus: 22000.0 - 22000.0 MPa
Processing Methods: Injection Molding
Markets: Electrical & Electronics
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Chemical Resistant
Good Flow
High Stiffness
High Temperature Resistance
Low Thermal Expansion
Wide Temperature Operating Range
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In a dry air (dessiccant) dryer 130-140 °C for 2-4 h; Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Automotive Applications
Holder
Housings
Machine/Mechanical Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

7 rows

Characteristic	Value	Unit	Method
Flexural Modulus	22000.0	MPa	ISO 178
Flexural Strength	220.0	MPa	ISO 178
Tensile Modulus	23000.0	MPa	ISO 527
Flexural Deflection (Maximum Force)	1.1	%	ISO 178
Tensile Strength at Break	150.0	MPa	ISO 527
Tensile Elongation at Break	1.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	25.0	kJ/m²	ISO 179/1eU

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density	1960.0	kg/m³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
HDT / A (1.8 MPa)	280.0	°C	ISO 75-1/-2
DSC (Melt Point)	280.0	°C	ISO 11357

Table 4 of 5

3 rows

Characteristic	Value	Unit	Method
Flammability (0.75 m)	V - 0	class	UL 94
Flammability (1.5 mm)	V - 0	class	UL 94
Glow Wire (GWFI, 960°C, 2mm)	Passed	—	DIN EN 60695

Table 5 of 5