ALCOM® MED PA66 1000 19046
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® MED PA66 1000 19046 has a minimum shelf life of 24 months and should be pre-dried at 80°C in a dry air (dessiccant) dryer for 2-12 hours depending on moisture content, with a maximum moisture content of less than 0.12%. The recommended processing injection molding melt temperatures are between 270-290°C and mold temperatures between 40-80°C. The base polymer is Polyamide 66, and it features easy release (demolding) and heat stabilization. It is suitable for the packaging, Medical / Personal Care market segments and can be used for injection molded parts of various shapes and sizes.
Product families
Applications
- Healthcare Packaging
- Non-Food Consumer Packaging
Product Families
- Polyamides
Other characteristics
- Brand
- ALCOM® MED
- Polymer Name
- Polyamide 66 (PA 66)
- Flexural Modulus
- 2900.0 - 2900.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Printing & Packaging
- Shelf LIfe
- Minimum 24 months
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Mold Release
- Heat Stabilized
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2900.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 90.0 | MPa | ISO 178 |
| Tensile Modulus | 2900.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 84.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 4.2 | % | ISO 527 |
| Tensile Elongation at Break | 20.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 130.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 4.5 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1140.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 75.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 263.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.12 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.6 - 2 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.5 - 1.9 | % | ISO 294-4 |