ALTECH® NXT PP -H A 2030/450.02 GF30 CP
MOCOM Compounds ALTECH® NXT PP -H A 2030/450.02 GF30 CP is a polypropylene homopolymer filled with 30% glass fibers, chemically coupled and high heat stabilized, providing high stiffness and high toughness. It is suitable for various injection molded parts in the automotive market segment. Processing injection molding requires a melt temperature of 200-250°C and a mold temperature of 20-70°C.
Product families
- Polyolefins
Other characteristics
- Brand
- ALTECH® NXT PP
- Features
Chemically Coupled, Excellent Toughness, Heat Aging Resistant, Heat Stabilized, High Performance, High Stiffness
- Functions
- Resin
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Material Features
- Chemically Coupled
- Excellent Toughness
- Heat Aging Resistant
- Heat Stabilized
- High Performance
- High Stiffness
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Plastics and Elastomers Functions
- Resin
- Performance Characteristics
E-Modulus over Different Temperatures Water/Glycol (50:50) Resistance at 120 °C Over Time
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6000.0 | MPa | ISO 178 |
| Flexural Strength | 145.0 | MPa | ISO 178 |
| Tensile Modulus | 7000.0 | MPa | ISO 527 |
| Tensile Strength at Break | 100.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 55.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 55.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 10.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 8.5 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1150.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 140.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 155.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 166.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 250 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 6.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.5 - 0.7 | % | ISO 294-4 |