ALTECH® ECO PP-H 4940/500 MR40

Chemical Family: PolyolefinsPolypropylenes (PP)

MOCOM Compounds ALTECH® ECO PP-H 4940/500 MR40 is a Polypropylene Homopolymer containing 40% talcum, antioxidant, heat stabilizer, impact modifier, processing stabilizer, easy release (demolding) agent, and recycled material. It is ideal for various injection molded parts. Pre-drying should be done in either a dry air (desiccant) dryer at 80-120°C for 2-3 hours, or in an air circulating dryer at 80-120°C for 2-4 hours. The melt temperature for Processing Injection molding should be 200-250°C and the mold temperature should be 20-70°C. Ensure that all components are completely dry before injection molding.

Product families

Plastics — Basic Thermoplastics

Polyolefins

Other characteristics

Brand: ALTECH® ECO
Polymer Name: Polypropylene Homopolymer (HPP)
Fillers Included: Mineral, Talc
Mineral
Talc
Additives Included: Antioxidant, Heat Stabilizer, Impact Modifier, Processing Stabilizer, Slip Agent; Antioxidant; Heat Stabilizer; Impact Modifier; Processing Stabilizer; Slip Agent
Processing Methods: Injection Molding
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Recycled
Material Features: Anti-Oxidant
Good Mold Release
Heat Stabilized
Impact Modified
Processing Stability
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

7 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2900.0	MPa	ISO 178
Flexural Strength	40.0	MPa	ISO 178
Tensile Modulus	2800.0	MPa	ISO 527
Tensile Strength	23.0	MPa	ISO 527
Tensile Elongation at Break	5.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	15.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	3.0	kJ/m²	ISO 179/1eA

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Density	1250.0	kg/m³	ISO 1183
Global Warming Potential (GWP)	0.93	kg CO₂ eq.	ISO 14040, 14044

Table 3 of 5

1 row

Characteristic	Value	Unit	Method
Vicat B50	85.0	°C	ISO 306

Table 4 of 5