ALCOM® PA6 900/1 GF30 WT1165-10LB
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA6 900/1 GF30 WT1165-10LB is a polyamide 6 base polymer filled with 30% glass fibers, featuring a highly reflective, opaque, and slip agent property. It is suitable for automotive, various lighting, light blocking components, and interior decoration/finishing applications such as light guides, reflectors, and handles. The recommended melt temperature range for processing injection molding is 270-290°C, and the mold temperature range is 80-100°C.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
- Interior
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Mineral
- Glass Fiber
- Mineral
- Additives Included
- Slip Agent
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Excellent Opacity
- Heat Aging Resistant
- High Reflectivity
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Handles
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 8700.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 4700.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 185.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 105.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 9400.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 4800.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 122.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.0 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 65.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 4.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 39.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1420.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 205.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 84.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.8 | % | ISO 13468 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.1 - 0.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |