MOCOM CompoundsALCOM® PC 730/5 UV WT1231-10LDX
MOCOM Compounds ALCOM® PC 730/5 UV WT1231-10LDX is a polycarbonate extrusion grade that is UV stabilized and contains a special filler. It is translucent, light scattering, and has high light diffusion, making it ideal for use as lamp covers and other light transparent components in automotive and lighting applications. The melt temperature for extrusion should be in the range of 240-280°C.
Brand:
- ALCOM
Polymer Name:
- Polycarbonate (PC)
Fillers Included:
- Proprietary
Flexural Modulus:
- 2500.0 - 2500.0 MPa
Additives Included:
- UV Stabilizer
Processing Methods:
- Extrusion, Injection Molding
Markets:
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
Technology:
- Plastics
Chemical Family:
- Polycarbonate (PC)
Labeling Claims:
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
Material Features:
- Good Light Diffusion
- High Light Diffusion
- Light Diffusing
- Light Scattering
- Translucent
- UV Resistant
- UV Stabilized
Storage Condition:
- Store in dry, protected from light.
Pre-Drying Conditions:
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- 120 °C in an air circulating dryer for 4-12 h
Certifications and Compliance:
- Directive 2011/65/EC amended through EU/2015/863 (RoHS)
- EC No.1907/2006
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- REACH (Europe)
- REACH (UK)
- RoHS Compliant
- SVHC Compliant
Plastics and Elastomers End Uses:
- Automotive Applications
- Lamp Covers
Plastics and Elastomers Functions:
- Resin
Plastics and Elastomers Processing Methods:
- Extrusion
- Injection Molding
Applications
Applications
- Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
- Automotive Lighting
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
| Characteristic name | Value | Unit of measurement | Test method |
| Flexural Modulus | 2500.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 76.0 | MPa | ISO 178 |
| Tensile Modulus | 2400.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 66.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 6.0 | % | ISO 527 |
| Tensile Elongation at Break | 50.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 15.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 15.0 | kJ/m² | ISO 179/1eA |
| Characteristic name | Value | Unit of measurement | Test method |
| Density | 1200.0 | kg/m³ | ISO 1183 |
| Characteristic name | Value | Unit of measurement | Test method |
| Vicat B50 | 143.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 129.0 | °C | ISO 75-1/-2 |
| Characteristic name | Value | Unit of measurement | Test method |
| Moisture Content | max. 0.02 | % | - |
| Characteristic name | Value | Unit of measurement | Test method |
| Total Transmission T(Y) (d=1,0mm, A, 2°) | 50.0 | % | ISO 13468 |
| Haze T(Y) (d=1.0 mm, A, 2°) | 96.0 | % | ISO 13468 |
| Half Power Angle T(Y) (d=1mm, A, 2°) | 57.0 | Degree | - |
| Characteristic name | Value | Unit of measurement | Test method |
| Glow Wire (GWFI, 850°C, 1mm) | Passed | - | DIN EN 60695 |
| Glow Wire (GWFI, 850°C, 2mm) | Passed | - | DIN EN 60695 |
| Characteristic name | Value | Unit of measurement | Test method |
| Melt Temperature | 240 - 280 | °C | - |
| Characteristic name | Value | Unit of measurement | Test method |
| Melt Index (MVR) | 4.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | - |
| MVR Load | 1.2 | kg | - |
| Shrinkage (24h) | 0.6 - 0.8 | % | ISO 294-4 |