ALCOM® PA46 920/1 PTFE15
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA46 920/1 PTFE15 is a polyamide 4.6-based filler/additive system with 15% PTFE, providing improved sliding/wear, heat stability, and is applicable to a range of market segments, such as machinery and automotive. Its applications include functional components, bearings, and sliding elements. To ensure optimal performance, the product should be pre-dried using 80°C in a dry air (dessiccant) dryer for 2-12 hours, dependent on the moisture content, with a maximum moisture content of 0.01%. For injection molding, the melt temperature should be 305-320°C and the mold temperature should be 40-100°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 46 (PA 46)
- Fillers Included
- PTFE
- Flexural Modulus
- 2800.0 - 2800.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Sliding Properties
- Heat Stabilized
- Improved Wear
- Wear Resistant
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2800.0 | MPa | ISO 178 |
| Flexural Strength | 110.0 | MPa | ISO 178 |
| Tensile Modulus | 2700.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 60.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 2.5 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 25.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 4.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1270.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 275.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 90.0 | °C | ISO 75-1/-2 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.01 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 305 - 320 | °C |
| Mould Temperature | 40 - 100 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.7 - 2 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.7 - 2 | % | ISO 294-4 |