ALCOM® PP 620/6 UV GY1380-05MCO
MOCOM Compounds ALCOM® PP 620/6 UV GY1380-05MCO is a gray, metallic, flow line optimized, and UV stabilized polypropylene homopolymer. It is suitable for pre-drying conditions in an air circulating dryer at 80-100°C for 2-4 hours, or in a dry air (dessiccant) dryer at 80-100°C for 2-3 hours, depending on moisture content. For injection molding, a melt temperature of 200-270°C and a mold temperature of 20-70°C are recommended. Typical applications include housings for household goods. To ensure the best performance, it should be kept dry and protected from light, not exceeding 30°C.
Product families
Applications
- Consumer Goods — Housewares
- Housings & Enclosures
Product Families
- Polyolefins
Other characteristics
- Brand
- ALCOM
- Features
- UV Resistant, UV Stabilized
- Functions
- Resin
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Additives Included
- UV Stabilizer
- Processing Methods
- Injection Molding
- Color
- Grey
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- UV Resistant
- UV Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-100 °C for 2-3 h; In an air circulatIng dryer 80-100 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Household Goods
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2200.0 | MPa | ISO 178 |
| Flexural Strength | 54.0 | MPa | ISO 178 |
| Tensile Modulus | 2200.0 | MPa | ISO 527 |
| Tensile Strength at Break | 39.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 11.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 34.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 930.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 106.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 72.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 163.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 270 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 30.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.6 - 2 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 2 | % | ISO 294-4 |