ALCOM® LDX PC 1000 UV 16069 GY1080-16
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds ALCOM® LDX PC 1000 UV 16069 GY1080-16 is a polycarbonate base polymer filled with a special filler system and UV stabilized. It is translucent, light scattering, and has high light diffusion. This extrusion grade is suitable for use in the lighting market for lamp covers and light transparent components. Processing extrusion should be done at a melt temperature of 240-280°C and it should be stored dry and protected from light.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Lighting
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Proprietary
- Flexural Modulus
- 2450.0 - 2450.0 MPa
- Additives Included
- UV Stabilizer
- Processing Methods
- Extrusion
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Light Diffusion
- High Light Diffusion
- Light Scattering
- Translucent
- UV Resistant
- UV Stabilized
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- 120 °C in an air circulating dryer for 4-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Lamp Covers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
Technical data
Table 1 of 8
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2450.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 76.0 | MPa | ISO 178 |
| Tensile Modulus | 2400.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 66.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 6.0 | % | ISO 527 |
| Tensile Elongation at Break | 65.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 12.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 12.0 | kJ/m² | ISO 179/1eA |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1190.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 142.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 124.0 | °C | ISO 75-1/-2 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Total Transmission T(Y) (d=1,0mm, A, 2°) | 29.5 | % | ISO 13468 |
| Total Transmission T(Y) (d=2,0mm, A, 2°) | 9.5 | % | ISO 13468 |
| Haze T(Y) (d=1.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Haze T(Y) (d=2.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Half Power Angle T(Y) (d=1mm, A, 2°) | 34.0 | Degree | — |
| Half Power Angle T(Y) (d=2mm, A, 2°) | 46.0 | Degree | — |
Table 6 of 8
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (0.75 m) | V - 2 | class | UL 94 |
| Flammability (1.5 mm) | HB | class | UL 94 |
| Glow Wire (GWFI, 850°C, 1mm) | Passed | — | DIN EN 60695 |
| Glow Wire (GWFI, 850°C, 2mm) | Passed | — | DIN EN 60695 |
| Fire Behavior FMVSS (1.0 mm) | Passed | — | FMVSS 302/DIN 75200 |
Table 7 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 240 - 280 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 7.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | 0.6 - 0.9 | % | ISO 294-4 |