CELLIDOR® CP 410-18

Chemical Family: Cellulose & Cellulosics

MOCOM Compounds CELLIDOR® CP 410-18 is a base polymer of Cellulose Acetate Propionate, which is processing stabilized and has a high toughness. It is typically used for various applications. Pre-drying conditions involve air-circulation in a dryer at 50-80°C for 2-4 hours, depending on the moisture content. During injection molding, the melt temperature should range from 180-230°C and the mold temperature from 40-80°C. It is phthalate-free and contains a plasticiser.

Product families

Plastics — Basic Thermoplastics

Cellulosics

Other characteristics

Brand: CELLIDOR
Density: 1180.0 - 1180.0 kg/m³
End Uses: Fishing Baits
Polymer Name: Cellulose Acetate Propionate (CAP)
Additives Included: Plasticizer (Phthalate-free), Processing Stabilizer; Plasticizer (Phthalate-free); Processing Stabilizer
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Bio-based
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Excellent Toughness
Non Phthalate Plasticizer
Processing Stability
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In an air circulatIng dryer 50-80 °C for 2-4 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Fishing Baits
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

12 rows

Characteristic	Value	Unit	Method
Flexural Modulus	1250.0	MPa	ISO 178
Flexural Strength	30.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	30.0	MPa	ISO 178
Tensile Modulus	1350.0	MPa	ISO 527
Tensile Stress at Yield	26.0	MPa	ISO 527
Tensile Elongation at Yield	3.0	%	ISO 527
Tensile Elongation at Break	30.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	no break	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	250.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	35.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	10.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H132/30)	50.0	MPa	ISO 2039-1

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density	1180.0	kg/m³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Vicat B50	70.0	°C	ISO 306
HDT / A (1.8 MPa)	60.0	°C	ISO 75-1/-2

Table 4 of 5