ALCOM® PBT/ASA 715/1 GF15 TF6 UV WT1287-09LB
MOCOM Compounds ALCOM® PBT/ASA 715/1 GF15 TF6 UV WT1287-09LB is a material composed of a base polymer of Polybutylene Terephthalate + Acrylonitrile Styrene Acrylate, a filler/additive system of 15% glass fibers and 6% PTFE, and special features of high reflectivity, opacity, and high stiffness, with UV stabilization. It is developed for the automotive and lighting industries and is suitable for light guides, reflectors, and light blocking components.
Product families
Applications
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
- Blends & Alloys
Other characteristics
- Brand
- ALCOM
- Density
- 1610.0 - 1610.0 kg/m³
- Polymer Name
- PBT/ASA Alloy
- Flexural Modulus
- 6100.0 - 6100.0 MPa
- Tensile Strength
- 82.0 - 82.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber
- Mineral
- PTFE
- Additives Included
- UV Stabilizer
- Material Features
- Excellent Opacity
- High Reflectivity
- High Stiffness
- Light Blocking
- UV Resistant
- UV Stabilized
- Wear Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-120 °C for 2-4 h; In an air circulatIng dryer 100-120 °C for 4-8 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6100.0 | MPa | ISO 178 |
| Flexural Strength | 125.0 | MPa | ISO 178 |
| Tensile Modulus | 6400.0 | MPa | ISO 527 |
| Tensile Strength at Break | 82.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 2.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 7.0 | kJ/m² | ISO 179/1eA |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1610.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 140.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 189.0 | °C | ISO 75-1/-2 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 90.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.6 | % | ISO 13468 |
Table 6 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 260 - 280 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 8 of 8
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 12.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 275.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.9 | % | ISO 294-4 |