ALCOM® PA66 910/1 MO2
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/1 MO2 is a polyamide 66 base polymer with 2% molybdenium disulphide filler/additive system that is improved for sliding/wear, heat-stabilized, and suitable for machinery, bearings, sliding elements, and functional components. It should be pre-dried in a dry air (dessiccant) dryer below 80°C for 2-12 hours, depending on the moisture content. During processing injection molding, the melt temperature should range from 270-290°C and the mold temperature should range from 40-80°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Molybdenum Disulfide
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Sliding Properties
- Good Tribological Properties
- Heat Stabilized
- Improved Wear
- Wear Resistant
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Bearings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 3150.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 1350.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 120.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 100.0 | MPa | ISO 178 |
| Flexural Stress (Conditioned, 3.5% Strain) | 37.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 3500.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 1400.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Dry) | 85.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Conditioned) | 58.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Conditioned) | 19.0 | % | ISO 527 |
| Tensile Elongation at Break (Dry) | 10.0 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 125.0 | % | ISO 527 |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1150.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 85.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 5 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Sliding Friction µ (pv = 2*1 MPa*m/s) | 0.6 | — | ASTM G 137 |
| Specific Wear Rate ws (pv = 2*1 MPa*m/s) | 3.0 | E⁻⁶ mm³/Nm | ASTM G 137 |
| Linear Wear Rate w (pv = 2*1 MPa*m/s) | 21.0 | µm/h | ASTM G 137 |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.7 - 0.9 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.8 - 1 | % | ISO 294-4 |