MOCOM Compounds ALCOM® TPU 810/3070.1 CF15 is a polyurethane estertype base polymer with 15% carbon fibers as filler/additive system, and is electrically conductive with reduced surface resistivity. It is applicable in automotive and machinery market segments and can be used for various purposes such as functional components. For optimal performance, it should be pre-dried in a dry air (dessiccant) dryer or air circulating dryer at 80-110°C for 1-3 hours with a maximum moisture content of <0.05%.
Identification
Product families
- Thermoplastic Urethanes (TPU)
Other characteristics
- Brand
- ALCOM
- Density
- 1250.0 - 1250.0 kg/m³
- End Uses
Automotive Applications, Machine/Mechanical Parts
- Features
Electrically Conductive, Reduced Surface Resistivity
- Polymer Name
- Thermoplastic Polyurethane (Polyester based)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Strain at Break
- 25.0 - 25.0 %
- Flexural Modulus
- 600.0 - 600.0 MPa
- Processing Methods
- Extrusion, Injection Molding
- Technology
- Elastomers
- Fillers Included
- Carbon Fiber
- Material Features
- Electrically Conductive
- Reduced Surface Resistivity
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-110 °C for 1-3 h; In an air circulatIng dryer 80-110 °C for 1-3 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 600.0 | MPa | ISO 178 |
| Flexural Strength | 20.0 | MPa | ISO 178 |
| Shore Hardness D (15s) | 55.0 | — | ISO 868 |
| Tensile Modulus | 600.0 | MPa | ISO 527 |
| Tensile Strength | 45.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 25.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 60.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1250.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 58.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 62.0 | °C | ISO 75-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.05 | % |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | max. 50 | Ohm | IEC 62631-3-2 |
Table 6 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 200 - 220 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 40 | °C |
| Melt Temperature | 210 - 230 | °C |