ALCOM® PA66 910/1.1 CF10
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/1.1 CF10 is a polyamide 66 base polymer with 10% carbon fibers, which is electrically conductive, heat stabilized, and has high stiffness. It is suitable for various applications, such as bearings and functional components, and is suitable for injection molding with a melt temperature of 280-300°C and a mold temperature of 80-120°C. Intended for the Automotive and Machinery market segments, it should be stored dry and protected from light to ensure optimal performance.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Carbon Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Electrically Conductive
- Good Abrasion Resistance
- Good Sliding Properties
- Heat Stabilized
- High Friction
- High Stiffness
- Reduced Surface Resistivity
- Wear Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Domestic Appliance Adapters
- Machine/Mechanical Parts
- Power Drill Mountings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 7400.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 220.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 8100.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 155.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.4 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 30.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 28.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1170.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 250.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance (Conditioned) | max. 700 | Ohm | IEC 62631-3-2 |
Table 6 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 7 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Sliding Friction µ (pv = 5*1 MPa*m/s) | 0.26 | — | ASTM G 137 |
| Coefficient of Sliding Friction µH (pv = 5*1 MPa*m/s) | 0.31 | — | ASTM G 137 |
| Specific Wear Rate ws (pv = 5*1 MPa*m/s) | 0.33 | E⁻⁶ mm³/Nm | ASTM G 137 |
| Linear Wear Rate w (pv = 5*1 MPa*m/s) | 5.9 | µm/h | ASTM G 137 |
Table 8 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.1 - 0.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |