MOCOM Compounds ALCOM® LD2 MBS 1000 UV 18013 WT1021-18 is a polystyrene copolymer that is translucent, has high light diffusion, light scattering, good flow, processing stabilized, and UV stabilized. It is an injection molding grade suitable for use in the automotive and lighting market segments and is typically used for lamp covers, display elements, and operating elements.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
- Automotive Lighting
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Product Families
Elastomers — Thermoplastic Elastomers
- Styrenic Thermoplastic Elastomers (TPE-S)
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Methyl Methacrylate Butadiene Styrene (MBS)
- Strain at Break
- 60.0 - 60.0 %
- Additives Included
- Processing Stabilizer, UV Stabilizer
- Processing Stabilizer
- UV Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Elastomers
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Light Diffusion
- High Light Diffusion
- Light Scattering
- Processing Stability
- Translucent
- UV Resistant
- UV Stabilized
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 65 °C in a dry air (dessiccant) dryer for 2-3 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Displays
- Lamp Covers
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 1600.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 37.0 | MPa | ISO 178 |
| Tensile Modulus | 1700.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 27.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 11.0 | % | ISO 527 |
| Tensile Elongation at Break | 60.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 20.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 10.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 2.0 | kJ/m² | ISO 179/1eA |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1040.0 | kg/m³ | ISO 1183 |
Table 3 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 61.0 | °C | ISO 306 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Total Transmission T(Y) (d=1,0mm, A, 2°) | 77.5 | % | ISO 13468 |
| Total Transmission T(Y) (d=2,0mm, A, 2°) | 62.5 | % | ISO 13468 |
| Total Transmission T(Y) (d=3,0mm, A, 2°) | 52.5 | % | ISO 13468 |
| Total Transmission T(Y) (d=4,0mm, A, 2°) | 45.0 | % | ISO 13468 |
| Haze T(Y) (d=1.0 mm, A, 2°) | 93.5 | % | ISO 13468 |
| Haze T(Y) (d=2.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Haze T(Y) (d=3.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Haze T(Y) (d=4.0 mm, A, 2°) | 95.5 | % | ISO 13468 |
| Half Power Angle T(Y) (d=1mm, A, 2°) | 2.0 | Degree | — |
| Half Power Angle T(Y) (d=2mm, A, 2°) | 28.0 | Degree | — |
| Half Power Angle T(Y) (d=3mm, A, 2°) | 44.0 | Degree | — |
| Half Power Angle T(Y) (d=4mm, A, 2°) | 52.0 | Degree | — |
Table 6 of 8
2 rows| Characteristic | Value | Method |
|---|---|---|
| Glow Wire (GWFI, 550°C, 1mm) | Passed | DIN EN 60695 |
| Glow Wire (GWFI, 550°C, 2mm) | Passed | DIN EN 60695 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 200 - 240 | °C |
| Mould Temperature | 30 - 60 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 75.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 220.0 | °C | — |
| MVR Load | 10.0 | kg | — |
| Shrinkage (24h) | 0.3 - 0.7 | % | ISO 294-4 |