ALCOM® LB ECO PC+ABS 1000 SL WT1023-21
MOCOM Compounds ALCOM® LB ECO PC+ABS 1000 SL WT1023-21 is a pre-dried injection molding grade with a polycarbonate + acrylonitrile butadiene styrene blend. It is highly reflective, contains recycled material, has anti-squeak modifications, and is opaque. It is used in the automotive, electrical and electronic, and lighting markets and is typically used for light guides and reflectors. When processing injection molding, the melt temperature should be 240-280°C and the mold temperature should be 70-100°C.
Product families
Applications
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
- Lighting
Product Families
- Blends & Alloys
Other characteristics
- Brand
- ALCOM
- Density
- 1260.0 - 1260.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2000.0 - 2000.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Recycled
- Additives Included
- Anti-Squeak Agent
- Material Features
- Anti-Squeaking
- Excellent Opacity
- High Reflectivity
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-110 °C for 2-4 h; In an air circulatIng dryer 100-110 °C for 3-6 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Electrical/Electronic Applications
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2000.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 60.0 | MPa | ISO 178 |
| Tensile Modulus | 2000.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 42.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 3.3 | % | ISO 527 |
| Tensile Elongation at Break | 75.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 255.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 220.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 65.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 83.0 | MPa | ISO 2039-1 |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1260.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 104.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 99.0 | °C | ISO 75-1/-2 |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 93.0 | % | DIN 5033 |
| Total Transmission T(Y) (d=2,0mm, A, 2°) | 0.0 | % | ISO 13468 |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 240 - 280 | °C |
| Mould Temperature | 70 - 100 | °C |
Table 6 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 17.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 260.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Shrinkage (24h) | 0.6 - 0.8 | % | ISO 294-4 |