ALCOM® PP 620/8 GF30 PTFE15
MOCOM Compounds ALCOM® PP 620/8 GF30 PTFE15 is a heat-stabilized polypropylene homopolymer with a 30% glass fiber and 15% PTFE filler/additive system. It is used in the automotive and machinery market segments for various applications and should be pre-dried either in a dry air (dessiccant) dryer at 80-100°C for 2-3 hours or in an air circulating dryer at 80-100°C for 2-4 hours, depending on the moisture content. Processing should be done with a melt temperature of 200-270°C and a mold temperature of 29-90°C.
Product families
- Polyolefins
Other characteristics
- Brand
- ALCOM
- Features
Good Sliding Properties, Heat Stabilized, Improved Wear, Wear Resistant
- Functions
- Resin
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Material Features
- Good Sliding Properties
- Heat Stabilized
- Improved Wear
- Wear Resistant
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-100 °C for 2-3 h; In an air circulatIng dryer 80-100 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6100.0 | MPa | ISO 178 |
| Flexural Strength | 125.0 | MPa | ISO 178 |
| Tensile Modulus | 6700.0 | MPa | ISO 527 |
| Tensile Strength at Break | 82.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.3 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 44.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 10.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 7.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1250.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 136.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 148.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 163.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 200 - 270 | °C |
| Mould Temperature | 29 - 90 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 2.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.4 - 0.6 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.4 - 0.6 | % | ISO 294-4 |