ALCOM® PA6 900/1 GF15 GB15
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA6 900/1 GF15 GB15 is a heat-stabilized, low-warpage polyamide 6 that contains 15% glass fibers and 15% glass beads. It is suitable for injection molding with a melt temperature of 270-290°C and a mold temperature of 80-100°C. This material is suitable for use in the automotive and machinery industries for various applications. For optimal performance, it should be stored in a dry, light-protected environment at temperatures not exceeding 30°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Bead, Glass Fiber
- Glass Bead
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Stabilized
- Low Warpage
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 5800.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 180.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 6400.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 115.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 3.9 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1340.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 197.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 222.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.3 - 0.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |