ALCOM® PA6 900/1 GF8 GB7

Chemical Family: Polyamides

MOCOM Compounds ALCOM® PA6 900/1 GF8 GB7 is a heat-stabilized, low-warpage polyamide 6 that can be processed with a melt temperature of 270-290°C and a mold temperature of 80-100°C. It consists of 8% glass fibers and 7% glass beads, and is designed for use in the automotive and machinery markets. To ensure optimal performance, it should be stored in a dry, light-protected environment not exceeding 30°C.

Product families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: ALCOM
Polymer Name: Polyamide 6 (PA 6)
Fillers Included: Glass Bead, Glass Fiber
Glass Bead
Glass Fiber
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Heat Stabilized
Low Warpage
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: 80 °C in a dry air (dessiccant) dryer for 2-12 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Automotive Applications
Machine/Mechanical Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

7 rows

Characteristic	Value	Unit	Method
Flexural Modulus (Dry)	4200.0	MPa	ISO 178
Flexural Strength (Dry)	150.0	MPa	ISO 178
Tensile Modulus (Dry)	4500.0	MPa	ISO 527
Tensile Strength at Break (Dry)	95.0	MPa	ISO 527
Tensile Elongation at Break (Dry)	3.5	%	ISO 527
Impact Strength (Dry, Charpy, at 23°C)	35.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Dry, Charpy, at 23°C)	4.0	kJ/m²	ISO 179/1eA

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density (Dry)	1230.0	kg/m³	ISO 1183

Table 3 of 5

3 rows

Characteristic	Value	Unit	Method
Vicat B50 (Dry)	208.0	°C	ISO 306
HDT / A (Dry, 1.8 MPa)	172.0	°C	ISO 75-1/-2
DSC (Melt Point, Dry)	221.0	°C	ISO 11357

Table 4 of 5

2 rows

Characteristic	Value	Unit
Melt Temperature	270 - 290	°C
Mould Temperature	80 - 100	°C

Table 5 of 5