Alcom® CFX ABS 1000 16012 SV1017-16MC

Chemical Family: Acrylonitrile Butadiene Styrene (ABS)Styrenics

MOCOM Compounds Alcom® CFX ABS 1000 16012 SV1017-16MC is a metallic-effect acrylonitrile/butadiene/styrene copolymer base polymer, designed for injection-molded parts, particularly housings. Prior to processing, it requires pre-drying in a dry air (dessiccant) dryer at 80°C for 2-4 hours or in an air circulating dryer for 3-6 hours, depending on the moisture content.

Product families

Applications

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Brand: ALCOM
Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Processing Methods: Injection Molding
Markets: Electrical & Electronics
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: 80 °C in a dry air (dessiccant) dryer for 2-4 h
80 °C in an air circulating dryer for 3-6 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Covers
Housings
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

1 row

Characteristic	Value	Unit	Method
Density	1050.0	kg/m³	ISO 1183

Table 2 of 5

11 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2600.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	64.0	MPa	ISO 178
Impact Strength (Charpy, at 23°C)	50.0	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	40.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	14.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	5.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H358/30)	96.0	MPa	ISO 2039-1
Tensile Elongation at Break	18.0	%	ISO 527
Tensile Elongation at Yield	2.2	%	ISO 527
Tensile Modulus	2500.0	MPa	ISO 527
Tensile Stress at Yield	42.0	MPa	ISO 527

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
HDT / A (1.8 MPa)	80.0	°C	ISO 75-1/-2
Vicat B50	93.0	°C	ISO 306

Table 4 of 5