Alcom® LB PC 1000 14073 WT1164-14
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds Alcom® LB PC 1000 14073 WT1164-14 is a polycarbonate-based injection molding grade polymer with a special filler/additive system that provides improved surface appearance and easy flow. This material is highly reflective and designed specifically for use in the automotive and lighting markets.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Electrical & Electronics — Devices & Assemblies
- Displays
Electrical & Electronics — Parts & Components
- Sensors & Actuators
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Mineral, Proprietary
- Mineral
- Proprietary
- Flexural Modulus
- 2600.0 - 2600.0 MPa
- Processing Methods
- Injection Molding
- Color
- White
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Light Reflection
- Good Surface Appearance
- High Reflectivity
- Light Blocking
- Radar Transparent
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- 120 °C in an air circulating dryer for 4-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Displays
- Light Blocking Components
- Light Guides
- Radomes
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1250.0 | kg/m³ | ISO 1183 |
Table 2 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2600.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 76.0 | MPa | ISO 178 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 10.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 8.5 | kJ/m² | ISO 179/1eA |
| Tensile Elongation at Break | 40.0 | % | ISO 527 |
| Tensile Elongation at Yield | 5.5 | % | ISO 527 |
| Tensile Modulus | 2400.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 63.0 | MPa | ISO 527 |
Table 3 of 7
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Dielectric Constant (εr) | 2.955 | — |
| Dielectric Constant (εr) | 2.955 | — |
| Dissipation Factor (tan δ) (at 77GHz, 2.3 mm) | 0.006 | — |
| Moisture Content | max. 0.02 | % |
Table 4 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 124.0 | °C | ISO 75-1/-2 |
| Vicat B50 | 137.0 | °C | ISO 306 |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 95.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 3.0 | % | ISO 13468 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 320 | °C |
| Mould Temperature | 80 - 110 | °C |
Table 7 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 35.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | 0.5 - 0.8 | % | ISO 294-4 |