ALCOM® PA66 910/32.1 TCE5
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/32.1 TCE5 is a polyamide 66 base polymer with a special filler and additive system that provides thermal and electrical conductivity, as well as heat stabilization. It is mainly used for automotive, machinery, electrical and electronic, and lighting applications like electrical components, radiator systems, and cooling systems such as housings and functional components. To ensure optimal performance, it should be pre-dried at 80°C in a dry air (dessiccant) dryer for 2-12 hours, with a maximum moisture content of 0.12%. For injection molding, the melt temperature should be between 300-320°C and the mold temperature should be between 100-130°C.
Product families
Applications
- Cooling & Climate
- Housings & Enclosures
- Sensors & Actuators
Product Families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Proprietary
- Flexural Modulus
- 6500.0 - 6500.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Electrically Conductive
- Good Thermal Conductivity
- Heat Stabilized
- High Anisotropy
- Reduced Surface Resistivity
- Thermally Conductive
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant; UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Cooling System
- Electrical Components
- Electrical/Electronic Applications
- Heat Sinks
- Housings
- Machine/Mechanical Parts
- Radiator Systems
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6500.0 | MPa | ISO 178 |
| Flexural Strength | 80.0 | MPa | ISO 178 |
| Tensile Modulus | 6000.0 | MPa | ISO 527 |
| Tensile Strength at Break | 50.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.5 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 10.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 2.5 | kJ/m² | ISO 179/1eA |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1340.0 | kg/m³ | ISO 1183 |
Table 3 of 8
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 220.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 263.0 | °C | ISO 11357 |
| Thermal Conductivity (integral) | 4.5 | W/(m K) | ISO 22007-2 |
| Specific Heat Capacity | 1.45 | J/gK | — |
| Thermal Conductivity (in-plane) | 8.0 | W/(m K) | ASTM E 1461 |
| Thermal Conductivity (through-plane) | 2.0 | W/(m K) | ASTM E 1461 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.12 | % |
Table 5 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | max. 5000 | Ohm | IEC 62631-3-2 |
Table 6 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (3.0 mm) | V - 0 | class | UL 94 |
| Glow Wire (GWFI, 960°C, 1mm) | Passed | — | DIN EN 60695 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 100 - 130 | °C |
| Melt Temperature | 300 - 320 | °C |
Table 8 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.6 - 0.9 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.9 | % | ISO 294-4 |