Alcom® PWL 10/1.1 WT1302-05LB
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds Alcom® PWL 10/1.1 WT1302-05LB is a polycarbonate injection molding grade material containing a special filler system of 15% that provides highly reflective and opaque properties. It is UV stabilized and provides easy release during demolding, and is often used in the automotive industry for lighting and light blocking components, such as light guides and reflectors.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Mineral, Proprietary
- Mineral
- Proprietary
- Flexural Modulus
- 2900.0 - 2900.0 MPa
- Additives Included
- UV Stabilizer
- Processing Methods
- Injection Molding
- Color
- White
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Excellent Opacity
- Good Light Reflection
- Good Mold Release
- High Reflectivity
- Light Blocking
- UL Listed
- UV Resistant
- UV Stabilized
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- 120 °C in an air circulating dryer for 4-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Control Panel
- Lamp Body
- Lamp Housing
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Strength | 100.0 | MPa | ISO 178 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Flexural Modulus | 2900.0 | MPa | ISO 178 |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 10.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 10.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Temperature | 137.0 | °C | DIN EN 60695-10-2 |
| Tensile Elongation at Break | 30.0 | % | ISO 527 |
| Tensile Elongation at Yield | 5.6 | % | ISO 527 |
| Tensile Modulus | 2900.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 63.0 | MPa | ISO 527 |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1360.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 129.0 | °C | ISO 75-1/-2 |
| Vicat B50 | 140.0 | °C | ISO 306 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 92.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.4 | % | ISO 13468 |
Table 6 of 8
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glow Wire (GWFI, 850°C, 2mm) | Passed | — | DIN EN 60695 |
| Glow Wire (GWFI, 850°C, 3mm) | Passed | — | DIN EN 60695 |
| Flammability (0.75 m) | HB | class | UL 94 |
| Flammability (1.5 mm) | HB | class | UL 94 |
| Flammability (3.0 mm) | HB | class | UL 94 |
| UL Recognition | yes | — | — |
| Yellow Card Available | yes | — | — |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 320 | °C |
| Mould Temperature | 80 - 110 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 15.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | 0.5 - 0.8 | % | ISO 294-4 |