ALCOM® POM 770/1 PTFE10
MOCOM Compounds ALCOM® POM 770/1 PTFE10 is a heat-stabilized, easy-release (demolding) and improved sliding/wear base polymer composed of Polyoxymethylene/general with 10% PTFE filler/additive system. It is suitable for various market segments and application areas and is processed via injection molding with a melt temperature of 180-220°C and mold temperature of 60-120°C. To ensure longevity, it should be stored in a dry, light-protected environment not exceeding 30°C.
Product families
- Polyacetals
Other characteristics
- Brand
- ALCOM
- Features
Good Mold Release, Good Sliding Properties, Heat Stabilized, Improved Wear, Wear Resistant
- Functions
- Resin
- Polymer Name
- Polyacetal Copolymer (POM)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- PTFE
- Flexural Modulus
- 2400.0 - 2400.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Material Features
- Good Mold Release
- Good Sliding Properties
- Heat Stabilized
- Improved Wear
- Wear Resistant
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-110 °C for 2-3 h; In an air circulatIng dryer 100-110 °C for 3-5 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2400.0 | MPa | ISO 178 |
| Flexural Strength | 80.0 | MPa | ISO 178 |
| Tensile Modulus | 2550.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 55.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 10.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 80.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1440.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 145.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 90.0 | °C | ISO 75-1/-2 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 180 - 220 | °C |
| Mould Temperature | 60 - 120 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 6.5 | cm³/10min | ISO 1133 |
| MVR Temperature | 190.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 1.8 - 2.2 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.6 - 2 | % | ISO 294-4 |