ALCOM® PC 740/4 UV SV1287-04MCS
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds ALCOM® PC 740/4 UV SV1287-04MCS is a polycarbonate-based material with a UV stabilized filler/additive system that has a metallic effect and easy flow properties. It is typically used for housings and applications such as clothing/fasteners and domestic appliances in the automotive, building and construction market segments.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Industrial — Leather & Textiles
- Textile Manufacturing
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polycarbonate (PC)
- Flexural Modulus
- 2550.0 - 2550.0 MPa
- Additives Included
- UV Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- UV Stabilized
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in a dry air (dessiccant) dryer for 2-3 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Construction Applications
- Fasteners
- Housings
- Textile Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2550.0 | MPa | ISO 178 |
| Flexural Strength | 100.0 | MPa | ISO 178 |
| Tensile Modulus | 2200.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 65.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 5.8 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 7.5 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1200.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 145.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 130.0 | °C | ISO 75-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (0.75 m) | V - 2 | class | UL 94 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 310 | °C |
| Mould Temperature | 80 - 110 | °C |
Table 7 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 24.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | min. 0.55 | % | ISO 294-4 |