ALCOM® PC 740/2813P.1 CF
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds ALCOM® PC 740/2813P.1 CF is a pre-dried polycarbonate featuring 10% carbon fibers, electrically conductive characteristics, reduced surface resistivity, and impact modification. It is typically used for injection molded parts in markets such as machinery and automotive, for applications such as housings and functional components. The recommended melt temperature is between 290-330°C and mold temperature 80-130°C. It should be kept in a dry, light-protected environment with a maximum moisture content of 0.02%. To ensure optimal performance, it is important to store this material in the recommended conditions.
Product families
Applications
- Housings & Enclosures
Product Families
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Carbon Fiber
- Flexural Modulus
- 6800.0 - 6800.0 MPa
- Additives Included
- Impact Modifier
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Electrically Conductive
- Impact Modified
- Reduced Surface Resistivity
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Housings
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6800.0 | MPa | ISO 178 |
| Flexural Strength | 160.0 | MPa | ISO 178 |
| Tensile Modulus | 7800.0 | MPa | ISO 527 |
| Tensile Strength at Break | 108.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 2.9 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 9.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1230.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 148.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 143.0 | °C | ISO 75-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | max. 1000 | Ohm | IEC 62631-3-2 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 290 - 330 | °C |
| Mould Temperature | 80 - 130 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.1 - 0.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.3 - 0.5 | % | ISO 294-4 |