ALCOM® PC 740/1 SV1115-08MCF

Chemical Family: Polycarbonate (PC)

MOCOM Compounds ALCOM® PC 740/1 SV1115-08MCF is a polycarbonate injection molding grade with a metallic effect and low tendency to flow lines. It is suitable for use in the automotive, building and construction markets. Pre-drying is recommended in a dry air (dessiccant) dryer at 100-120°C for 2-3 h depending on moisture content, with a maximum moisture content of 0.02%. For injection molding, a melt temperature of 270-310°C and a mold temperature of 80-110°C should be used. Additionally, it should be stored in the dark.

Product families

Applications

Industrial — Leather & Textiles

Textile Manufacturing

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Other characteristics

Brand: ALCOM
Polymer Name: Polycarbonate (PC)
Flexural Modulus: 2600.0 - 2600.0 MPa
Processing Methods: Injection Molding
Markets: Electrical & Electronics
Industrial
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Storage Condition: Store in dry, protected from light.
Pre-Drying Conditions: In a dry air (dessiccant) dryer 100-120 °C for 2-3 h; Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Automotive Applications
Construction Applications
Fasteners
Housings
Textile Applications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

10 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2600.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	75.0	MPa	ISO 178
Tensile Modulus	2500.0	MPa	ISO 527
Tensile Stress at Yield	61.0	MPa	ISO 527
Tensile Elongation at Yield	5.6	%	ISO 527
Tensile Elongation at Break	8.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	125.0	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	125.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	6.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	6.0	kJ/m²	ISO 179/1eA

Table 2 of 7

1 row

Characteristic	Value	Unit	Method
Density	1220.0	kg/m³	ISO 1183

Table 3 of 7

2 rows

Characteristic	Value	Unit	Method
Vicat B50	143.0	°C	ISO 306
HDT / A (1.8 MPa)	130.0	°C	ISO 75-1/-2

Table 4 of 7