ALCOM® PA66 910/8 IM SV1246-07MCF
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/8 IM SV1246-07MCF is a polyamide 66 base polymer with a silver, metallic effect and low tendency to flow lines. It is impact modified and heat-stabilized, and is suitable for injection molding with a melt temperature of 270-290°C and a mold temperature of 40-80°C. Mainly used for automotive and machinery applications for functional components and housings, this polymer is an excellent choice.
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Additives Included
- Heat Stabilizer, Impact Modifier, UV Stabilizer
- Heat Stabilizer
- Impact Modifier
- UV Stabilizer
- Processing Methods
- Injection Molding
- Color
- Silver
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Stabilized
- Impact Modified
- UV Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Housings
- Machine/Mechanical Parts
- Safety Helmets
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 1600.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 40.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 1700.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 30.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 20.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1100.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 60.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 264.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.7 - 2.1 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.4 - 1.8 | % | ISO 294-4 |