ALCOM® PBT 700/1.1 CF20 PTFE15
- Chemical Family
- Polyesters
MOCOM Compounds ALCOM® PBT 700/1.1 CF20 PTFE15 is a polybutylene terephthalate base polymer with 20% carbon fibers and 15% PTFE, designed for use in machinery applications and injection molded parts. It is electrically conductive, has reduced surface resistivity and improved sliding/wear, and is heat stabilized. The pre-drying conditions are in a dry air (dessiccant) dryer 100-120°C for 2-4 hours, or in an air circulating dryer 100-120°C for 4-8 hours depending on moisture content. The processing injection molding melt temperature is 250-270°C and the mold temperature is 80-120°C. The product should be handled with care to avoid any damage.
Product families
Applications
- Housings & Enclosures
Product Families
- Polyesters & Copolyesters
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Carbon Fiber, PTFE
- Carbon Fiber
- PTFE
- Flexural Modulus
- 14100.0 - 14100.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Electrically Conductive
- Good Sliding Properties
- Heat Stabilized
- Improved Wear
- Reduced Surface Resistivity
- Wear Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-120 °C for 2-4 h; In an air circulatIng dryer 100-120 °C for 4-8 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Housings
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 14100.0 | MPa | ISO 178 |
| Flexural Strength | 210.0 | MPa | ISO 178 |
| Tensile Modulus | 16200.0 | MPa | ISO 527 |
| Tensile Strength at Break | 140.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.6 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 37.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 6.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1470.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 210.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 217.0 | °C | ISO 75-1/-2 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | max. 25 | Ohm | IEC 62631-3-2 |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 1.1 | % | ISO 294-4 |