ALCOM® PBT 700/12 PTFE10
- Chemical Family
- Polyesters
MOCOM Compounds ALCOM® PBT 700/12 PTFE10 is a Polybutylene Terephthalate-based material containing 10% PTFE. It has improved sliding/wear properties, is heat-stabilized, and has good flow properties. It is used for functional components in the Automotive and Machinery markets and should be processed via injection molding at a melt temperature of 250-270°C and a mold temperature of 60-100°C.
Product families
- Polyesters & Copolyesters
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- PTFE
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Sliding Properties
- Heat Stabilized
- Improved Wear
- Wear Resistant
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-120 °C for 2-4 h; In an air circulatIng dryer 100-120 °C for 4-8 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2500.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 74.0 | MPa | ISO 178 |
| Tensile Modulus | 2400.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 50.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 4.8 | % | ISO 527 |
| Tensile Elongation at Break | 11.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 52.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 55.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1380.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 182.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 60.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 225.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 60 - 100 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 20.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 250.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.6 - 1.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.8 - 1.8 | % | ISO 294-4 |