ALCOM® PA66 910/1 MO1
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/1 MO1 is a polyamide 66 base polymer that contains 1% molybdenium disulphide, which gives it improved sliding/wear and heat stabilized features. It is typically used in machinery, bearings, sliding elements, and functional components. Injection molding should be employed to process this material, with a melt temperature of 270-290°C and a mold temperature of 40-80°C. To ensure longevity, it should be stored in the dark at temperatures not exceeding 30°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Molybdenum Disulfide
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Sliding Properties
- Heat Stabilized
- Improved Wear
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Bearings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 3100.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 1350.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 100.0 | MPa | ISO 178 |
| Flexural Stress (Conditioned, 3.5% Strain) | 30.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 3400.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 1500.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Dry) | 85.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Conditioned) | 58.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Dry) | 4.1 | % | ISO 527 |
| Tensile Elongation at Yield (Conditioned) | 10.0 | % | ISO 527 |
| Tensile Elongation at Break (Dry) | 17.0 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 19.0 | % | ISO 527 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1140.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 86.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 260.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.6 - 1.8 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.6 - 1.8 | % | ISO 294-4 |