ALCOM® PA6 900/1 CF10 IM
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA6 900/1 CF10 IM is a heat-stabilized, impact-modified polyamide 6 base polymer containing 10% carbon fibers, which is electrically conductive and has reduced surface resistivity. It is designed for use in the automotive and machinery industries for injection molding parts such as bearings, sliding elements, and functional components. The pre-drying conditions for ALCOM® PA6 900/1 CF10 IM are 80°C in a dry air (desiccant) dryer for 2-12 h, with a maximum moisture content of <0.15%. The melt temperature for injection molding should be between 270-290°C, and the mold temperature should be between 80-100°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Carbon Fiber
- Additives Included
- Heat Stabilizer, Impact Modifier
- Heat Stabilizer
- Impact Modifier
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Electrically Conductive
- Heat Stabilized
- Impact Modified
- Reduced Surface Resistivity
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 6300.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 3700.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 180.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 105.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 8400.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 4500.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 130.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 4.0 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 90.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 10.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 60.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 90.0 | kJ/m² | ISO 179/1eU |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1130.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 204.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 221.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance (Conditioned) | max. 7800 | Ohm | IEC 62631-3-2 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.3 - 0.5 | % | ISO 294-4 |