To catalogue
ALCOM® LB PC 1000 16061 GY1068-16
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds ALCOM® LB PC 1000 16061 GY1068-16 is a polycarbonate base polymer with a special filler/additive system that is highly reflective and opaque. It is used in the automotive and lighting market segments for lighting and light blocking components, such as light guides and reflectors. It is processed with injection molding using a melt temperature of 280-320°C and a mold temperature of 80-110°C.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Proprietary
- Flexural Modulus
- 2600.0 - 2600.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Excellent Opacity
- Good Light Reflection
- High Reflectivity
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- 120 °C in an air circulating dryer for 4-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2600.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 76.0 | MPa | ISO 178 |
| Tensile Modulus | 2400.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 62.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 5.9 | % | ISO 527 |
| Tensile Elongation at Break | 80.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 12.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 10.0 | kJ/m² | ISO 179/1eA |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1230.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 142.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 129.0 | °C | ISO 75-1/-2 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 31.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.1 | % | ISO 13468 |
Table 6 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (0.75 m) | V - 2 | class | UL 94 |
| Flammability (1.5 mm) | HB | class | UL 94 |
| Glow Wire (GWFI, 850°C, 1mm) | Passed | — | DIN EN 60695 |
| Glow Wire (GWFI, 850°C, 2mm) | Passed | — | DIN EN 60695 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 320 | °C |
| Mould Temperature | 80 - 110 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 15.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | 0.7 - 0.9 | % | ISO 294-4 |