ALCOM® HP PA6 7010 FR SB1000-20
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® HP PA6 7010 FR SB1000-20 is a heat stabilized, impact modified, halogen-free flame retardant, injection molding grade, high stiffness, electrostatically dissipating polyamide 6 with carbon fiber filler/additive system. It is designed for the electrical and electronic and machinery market segments and is suitable for injection molded parts. It should be pre-dried in a dry air (desiccant) dryer below 80°C for 2-12 hours, depending on moisture content, before processing with injection molding and a melt temperature of 270-290°C and mold temperature of 80-100°C. Additionally, it should be stored in a place with a temperature not exceeding 30°C and protected from light.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Carbon Fiber
- Additives Included
Flame Retardant, Heat Stabilizer, Impact Modifier; Flame Retardant; Heat Stabilizer; Impact Modifier
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Bacteria Resistant
- Flame Retardant
- Heat Stabilized
- High Stiffness
- Impact Modified
- Static-Dissipative
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Electrical/Electronic Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 7600.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 4800.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 165.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 105.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 8700.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 5300.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 110.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 4.4 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 74.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 8.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 55.0 | kJ/m² | ISO 179/1eU |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1190.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 204.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance (Conditioned) | max. 3500 | Ohm | IEC 62631-3-2 |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 3 mm) | V - 0 | class | UL 94 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.1 - 0.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.4 - 0.6 | % | ISO 294-4 |