ALCOM® AWL 15/2 WT1471-04LB
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
MOCOM Compounds ALCOM® AWL 15/2 WT1471-04LB is a base polymer of Acrylonitrile/Butadiene/Styrene/Copolymer filled with 15% special filler. It is highly reflective, opaque, and has good flow. This polymer is mainly used in lighting and light blocking components such as light guides and reflectors, primarily in the automotive market segment. For injection molding, it requires a melt temperature of 220-260°C and a mold temperature of 50-80°C. It should be stored in a dry place, away from direct light.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Mineral, Proprietary
- Mineral
- Proprietary
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Excellent Opacity
- Good Flow
- Good Light Reflection
- High Reflectivity
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-4 h
- 80 °C in an air circulating dryer for 4-8 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2800.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 63.0 | MPa | ISO 178 |
| Tensile Modulus | 2600.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 41.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 2.1 | % | ISO 527 |
| Tensile Elongation at Break | 10.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 30.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 105.0 | MPa | ISO 2039-1 |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1170.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 95.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 85.0 | °C | ISO 75-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 93.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.4 | % | ISO 13468 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 220 - 260 | °C |
| Mould Temperature | 50 - 80 | °C |
Table 7 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 25.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 220.0 | °C | — |
| MVR Load | 10.0 | kg | — |
| Shrinkage (24h) | min. 0.5 | % | ISO 294-4 |