ALCOM® AWL 10 WT1308-05LB
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
MOCOM Compounds ALCOM® AWL 10 WT1308-05LB is a base polymer composed of Acrylonitrile/Butadiene/Styrene/Copolymer containing 10% special filler. It has special features such as high reflectivity and opacity and is used for automotive and lighting applications, such as light guides and reflectors. To process this polymer, injection molding with a melt temperature of 220-260°C and a mold temperature of 50-80°C should be used. It should also be stored in a dry, light-protected area.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Mineral, Proprietary
- Mineral
- Proprietary
- Processing Methods
- Injection Molding
- Color
- White
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Excellent Opacity
- Good Light Reflection
- High Reflectivity
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-4 h
- 80 °C in an air circulating dryer for 4-8 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Control Panel
- LED Housing
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2600.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 73.0 | MPa | ISO 178 |
| Tensile Modulus | 2800.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 50.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 2.8 | % | ISO 527 |
| Tensile Elongation at Break | 13.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 80.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 12.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 115.0 | MPa | ISO 2039-1 |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1110.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 110.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 88.0 | °C | ISO 75-1/-2 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 85.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.2 | % | ISO 13468 |
Table 6 of 8
2 rows| Characteristic | Value | Method |
|---|---|---|
| Glow Wire (GWFI, 650°C, 1mm) | Passed | DIN EN 60695 |
| Glow Wire (GWFI, 650°C, 2mm) | Passed | DIN EN 60695 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 220 - 260 | °C |
| Mould Temperature | 50 - 80 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 6.5 | cm³/10min | ISO 1133 |
| MVR Temperature | 220.0 | °C | — |
| MVR Load | 10.0 | kg | — |
| Shrinkage (24h) | 0.3 - 0.6 | % | ISO 294-4 |